Crack (from Spurs): wire surface visible to the naked eye a small section of the horizontal crack, or other shape of a tongue of thorns

Stratification: vertical wire length of partial or split

Scarring (plaques scar): yellow wire surface oxidation scars, white lime scar

trace: vertical steel surface of the apparent existence of a small groove or convex edge, only to make minor non-smooth surface of the illuminated phenomenon.

Folding: wire along the length direction of the surface of the metal overlap linear, but also showed the formation of or zigzag curve. Metallographic examination, folded normally have iron oxide inclusions and decarburization layer.

Concave: wire on the surface of local depression.

 

Corrosion: steel surface and the overall partial oxidation phenomenon.

Ma points: wire surface oxidation when serious punctate or patchy distribution of the pits.

Bamboo: wire along the longitudinal cyclical uneven thickness, the shape of the United States may bamboo.

Spiral pattern: wire in the straightening process, the surface of the screw-shaped roller printed.

Oxide: wire surface and high temperature oxidation furnace gas exposure occurs when oxidation, producing a layer of hard oxide fracture easily.

Oxide film: a thin surface layer of steel wire dense oxides, such oxides generally difficult to fragmentation, were affected only when bending or deformation can be partially off.

Oxidation of color: bright steel surface under the conditions of heat treatment to generate a layer of very thin steel wire firmly attached to the surface oxides.

Decarburization Layer: wire heating due to gas media and the role of the carbon steel layer, so that the surface area to reduce the carbon content, which reduced the surface carbon is called decarbonization.

 

Graphite carbon: steel in some or all of the carbon to the free state analysis, which exist in the free state of carbon-carbon Ishiguro.

Crease: net surface locally folded to form a non-restored prints.
Hole: net surface concentration has multiple warp or weft wire break.

 
Corrosion: net surface corrosion deterioration

mesh surface green, brown or Harmonia small spots

Broken wires: network face warp or weft single to disconnect.

Mosquito mouth: wire, twist together and air out the network side.

Top deduction: warp bad joints, top of the net surface.

Reduced latitude: latitude local cubic curve mesh deformation.

And wire: two or more than two parallel metal wires woven together.

Wire jump  warp or weft woven cloth Board error.

loose wire: warp or parallel loosening of individual displacement.

Debris weaving: weaving foreign body in the mesh.

Cloud Texture: latitude had caused uneven soft or hard and soft rules of cloud-free map.

Drum Pack: Mesh out regional.

Lane: warp or weft overlap.

Hole Size: Mesh size of the uneven mesh regularity.

Dilute Micronesia file: Mesh sudden individual mesh is too large or too small.

Pine Edge: network edge drum-shaped waves process.

Diameter - is the wire diameter

Warp - weaving all of the vertical line

Latitude - all braided line horizontal

Mesh - 1 inches in length with the number of mesh

 

Density - 1 cm length of the number of mesh

Mesh - two by wire or two the distance between the weft yarn

Tolerance - Fully straight angle, the Integrated Department of warp-chip line with the tolerance of the vertical distance (MM)

Public line - before and after the chest had fruit (Laura) connection

On tolerance - Integrated chip Integrated peacetime Department warp higher than the tolerance line

Under tolerance - lower than the tolerance line under the name of tolerance

Zero tolerance - and tolerance is called zero tolerance line coincidence

Fully angle - Fully opening the box, after the fully-mechanized and mechanized distance under